CLOSED ON: 02 FEB 2020  |  REWARD: INR 5,00,000
Reward money is paid in exchange of legally acquiring the solution, implementing it to solve the problem and meeting the success criteria. Milestones for paying the reward money would depend upon the complexity of challenge and maturity of the proposed solution, which would be discussed with the solver as soon as the proposed solution is selected by us.

Short Description:

Develop an alternate method of glass joint assembly which is universal for all designs and shapes

Challenge Details

Any wristwatch has three major components, namely,

  1. Watch case, which is housing the mechanism,
  2. The mechanism or module with dials & hands,
  3. The strap to wear the watch on hand.

In watch case assembly, case center, back cover (BC), case pipe (CP), and glass are assembled on the watch case blank (made of metal) and later tested for joint-strength and water resistance (WR).  The WR test is a mandatory statutory requirement for watches and is done through a water immersion method where watch cases are soaked in the water for 10 minutes with the pressure of 5 Kg/cm2 or 7 Kg/cm2, based on specification.

To attain this WR property, all the joints mentioned above should have specified strength i.e. glass joint to withstand a minimum of 4 Kg/ cm2, BC joint to withstand a minimum of 5 Kg/ cm2 and CP to withstand minimum pressure of 3 Kg/ cm2. This strength will ensure the mating parts are intact when the watch is worn while riding a two-wheeler, running, jumping, etc., as well as resisting entry of water/moisture during testing/use because of outside pressure being higher.

As per horology standard and know-how, a glass joint is made by either of the following methods:

  1. Plastic gasket
  2. Adhesive
  3. Sticker
  4. Ultrasound welding in case of acrylic/plastic.

Each of these methods will have a certain advantage for each kind of design or configuration and quality. Based on the design of the watch case, the type of joint mechanism to be employed is chosen. Adhesive type joint is to be used:

1. If the model case is shaped and there is no housing/wall for the glass

2. Corners are sharp

3. Glass is having a gradient

 However, with the adhesive type joint being used currently, moderate WR is achieved. Also, the failure of watch cases is more prominent in this type. Thus, we are looking for alternate adhesives that can address these problems. Hence, the challenge is to ideate and implement an alternate innovative method of adhesive type joint between the glass and metallic parts, which is universal for all designs.

This will result in the flowing:

  1. Productivity increase
  2. Reliability ensured
  3. Design support
  4. No conditions imposed on watch designers and watch case assembly units.

Options Tried:

  • Sticker type joint was tried where the pressure-sensitive adhesive is used. It demands metallization (metallic coating of the plastic component) band-width of 1.5mm.
  • Hot melt glue, which forms a sticker type joint when it is heated at 120 oC for 1 hour, was also tried. However, such high temperatures have an adverse effect on plating quality.

Solution Requirements:

  • The alternate adhesive should be applicable for all the watch cases requiring adhesive type joint.
  • The method of applying adhesives should be universal for all designs and meet all desired requirements.  
  • It should not pose any restriction or constraint on the design or shape of the watch case.
  • The adhesive should not require significant pre or post-treatment after application on the watch cases.
  • It should provide high WR (up to 25 ATM for diving purposes) even in asymmetric shapes.
  • Any shock load shouldn’t induce hairline cracks or other failures in WR.
  • The new adhesive should provide higher quality at optimal cost with ease of production for the manufacturer.
  • Also, this alternate method should prevail throughout the world, i.e., it should have no geographical constraints.
  • The customer should be able to use and operate all types of watches, without knowing the preconditions of any watch type.

Have any query or need more clarification about this challenge?